    哪些因素会导致环氧树脂地坪涂层破坏

    2018-10-19 09:29:48 无锡盛发地坪科技有限公司 阅读

    众所周知,环氧树脂地坪是一种高强度、耐磨损、雅观的地板,拥有合座无接缝,质料结实,耐药品质佳,防腐,防水,防尘,调养简便,爱护费用低廉等优势.环氧树脂地坪起始是用于功能性环氧地坪:如防腐,耐磨,防滑,发展到通用的寻常产业环氧地坪;除去拥有功能性的要求,还拥有装饰性的功效.环氧树脂地坪通常的运用寿命在8-15年,但不少的停车场环氧树脂地坪往往在2-3年,甚而更短的时光内就会出列涂层的剥离毁坏的状况.底下咱们来解析一下停车场环氧树脂地坪涂层出列此类状况的缘故地点.

    As we all know, epoxy floor is a kind of high strength, wear-resistant, elegant floor, with seamless, strong materials, good resistance quality, corrosion, waterproof, dust-proof, easy maintenance, low cost of care and other advantages. Epoxy floor is originally used for functional floors: such as anti-corrosion, wear-resistant, skid-proof, to develop into a general purpose of ordinary industrial areas. Epoxy floors usually last 8-15 years, but many parking lot floors are usually stripped in 2-3 years, or even less. Let's analyze the epoxy floors in the parking lot. List the locations of such cases.

    环氧树脂地坪涂层出列隆起及裂痕:环氧树脂地坪涂层片面隆起,重点呈现为出列直径2~5mm以及30~50mm差异水准的隆起,重点缘故是下层干枯不能够,气体围拢在漆膜底下,涂膜面汲取水份而隆起,或许是由漆膜固化时有杂质未整理清洁.涂层出列裂痕,呈现为涂膜紧缩开裂以及涂层因下层裂痕而拉裂.

    Epoxy Floor Coatings Protrude and Cracks: Epoxy Floor Coatings are one-sided protrusions, with emphasis on protrusions of 2-5mm in diameter and 30-50mm in different levels. The main reason is that the underlying layer is not dry enough, the gas surrounds the film, and the surface of the film absorbs moisture, which may be caused by impurities not cleaned up when the film solidifies. The cracks in the coating appear as a tight crack in the coating and the cracking of the coating due to the cracks in the lower layer.

    停车场环氧树脂地坪涂层剥离毁坏:环氧树脂地坪涂层大面积剥离毁坏重点有两种状况:环氧树脂层与混凝土下层融合界面毁坏,呈现为环氧涂层零落,混凝土下层正常无损,大面积出列,直接缘故是界面黏结力不及;环氧涂层与混凝土下层表面沙浆融合密切,毁坏面出列在混凝土下层里面,毁坏面坐落混凝土下层的沙浆平面.

    Epoxy resin flooring coating peeling damage: Epoxy resin flooring coating peeling damage in a large area of two key conditions: epoxy resin layer and concrete layer fusion interface damage, showing epoxy coating scattered, concrete layer normal non-destructive, large area out of line, the direct reason is that the interface bonding force between epoxy coating and concrete; The mortar on the lower surface fuses closely, and the destroyed surface appears in the lower concrete layer, and the destroyed surface lies in the mortar plane of the lower concrete layer.

    这类毁坏模式通常大面积出列,直接缘故是混凝土的抗拉强度不及.停车场环氧树脂地坪涂层的差异涂膜层也有出列剥离的状况,重点缘故是差异涂膜之间的黏结力不及,通常出列于片面,大面积出列并不常见.

    This kind of damage mode usually appears in large area, the direct reason is that the tensile strength of concrete is less than. The different coatings of epoxy resin floor coatings in parking lot are also peeled off. The key reason is that the adhesion between different coatings is less than, usually listed in one-sided, large area is not common.