    分享解读环氧地坪工程的施工工艺流程

    2019-08-10 10:49:12 无锡盛发地坪科技有限公司 阅读

    环氧地坪工程的施工工艺流程:素地处理——底漆层施工——环氧砂浆修补找平层——环氧腻子层——面漆层施工--罩光层施工。环氧地坪工程的施工工艺流程一、素地处理1、将伸缩缝内的沥青或泥土掏出,并且清理干净。2、用材料填充伸缩缝。3、待地面完全干透后,将地面打磨干净,并完成对素地的处理。a.研磨机将地面轻轻打磨。其主要功能是将微小颗粒研磨在地面上,扩大表面孔隙,便于环氧树脂的吸附。b.增加环氧地坪的施工厚度,主要功能是耐压性和耐磨性,从而延长使用寿命。

    Construction process of epoxy floor project: plain ground treatment - primer layer construction - epoxy mortar repair leveling layer - epoxy putty layer - topcoat layer construction - covering layer construction. The construction process of the epoxy floor project is as follows: 1. plain treatment 1. The asphalt or soil in the expansion joint is taken out and cleaned up. 2. Fill expansion joint with material. 3. When the ground is completely dry, the ground will be polished and the vegetable land will be treated. A. The ground is lightly polished by a grinder. Its main function is to grind small particles on the ground, expand surface pore, and facilitate the adsorption of epoxy resin. B. To increase the construction thickness of epoxy floor, the main functions are pressure resistance and wear resistance, thus prolonging the service life. 二、底漆层施工

    II. Primer Layer Construction


    1、施工前保持清洁,如有附着杂物,应及时清除杂物。

    1. Keep clean before construction. If there is any attached sundries, they should be removed in time.


    2、将主剂和固化剂按正确的比例混合均匀。

    2. Mix the main agent and curing agent in the right proportion.


    3、应根据地面情况调整粘度。

    3. Viscosity should be adjusted according to ground conditions.


    4、用混合材料完成这项工程所需时间少于4小时。

    4. It takes less than 4 hours to complete the project with mixed materials.


    5、底漆硬化时间为8小时以上。

    5. The hardening time of primer is more than 8 hours.


    a.在环氧底漆施工过程中,根据不同的地基条件,在树脂吸附时,加入适量的石英粉密封表面气孔。

    A. During the construction of epoxy primer, according to different foundation conditions, proper amount of quartz powder is added to seal surface pore when resin is adsorbed.


    b.根据不同的表面硬度和孔径,施工后的效果是不同的。当树脂快速吸收时,残留在表面的石英粉松散而不固化,颜色呈白色。当树脂缓慢吸收时,石英粉与树脂固化。

    B. According to different surface hardness and aperture, the effect after construction is different. When the resin is absorbed rapidly, the quartz powder remaining on the surface is loose but not cured, and the color is white. When the resin slowly absorbs, quartz powder solidifies with the resin.


    三、环氧砂浆修补找平层

    3. Epoxy Mortar Repair Leveling Layer


    1、准备必要的工具和维护用品。

    1. Prepare necessary tools and maintenance supplies.


    2、确定修理区域。

    2. Determine the repair area.


    3、清除修补区混凝土基层表面的灰尘和油污,并清除松动的部分。

    3. Clean up the dust and oil on the surface of the concrete base in the repair area and remove the loose parts.


    4、清理修理区域裸钢表面的锈迹和碎片。

    4. Clean up rust and debris on bare steel surface in repair area.


    5、修复区的混凝土基层将进行清理、凿除或采用混凝土界面处理剂进行处理。

    5. The concrete base of the repair area will be cleaned up, chiseled out or treated with concrete interface treatment agent.


    6、用气泵或水清洗修补过的地方和混凝土基层表面。在下一道工序中不准有明水。

    6. Clean repaired areas and concrete base surfaces with air pump or water. No clear water is allowed in the next process.


    a.将两组分按比例称重后,将它们放入一个干净的备用桶中,搅拌均匀。加入适量的水调整混合,加入砂浆搅拌即可使用。混合好的添加剂在使用期内用完,需尽快施工水性环氧砂浆。

    After weighing the two components proportionally, they are put into a clean spare bucket and stirred evenly. Add appropriate amount of water to adjust the mixing, add mortar mixing can be used. Water-borne epoxy mortar should be constructed as soon as possible when the mixed additives are used up during the service life.


    b.事先清理旧界面的灰尘和渣滓,并使用水性环氧稀释剂(水性环氧树脂:水性环氧固化剂:水=1:1.3:3-5)。先把旧界面刷一遍,然后再施工水泥砂浆。

    B. Clean up the dust and dregs of the old interface beforehand and use water-borne epoxy diluent (water-borne epoxy resin: water-borne epoxy curing agent: water = 1:1.3:3-5). First brush the old interface, then construct the cement mortar.


    四、环氧腻子层(两道)

    4. Epoxy Putty Layer (Two Ways)


    1、根据正确的比例混合主剂和固化剂,并彻底搅拌。

    1. Mix the main agent and curing agent according to the correct proportion and stir thoroughly.


    2、混合后加入适量的石英粉。

    2. Adding proper amount of quartz powder after mixing.


    3、使用批刀均匀涂布材料。

    3. Use batch knife to coat material evenly.


    4、完成混合物料的施工,所需时间少于30分钟。

    4. It takes less than 30 minutes to complete the construction of mixture material.


    5、环氧腻子层的硬化时间为8小时以上。

    5. The hardening time of epoxy putty layer is more than 8 hours.


    a.环氧腻子层的主要作用是增加环氧地坪厚度,使其更耐压、耐磨,延长使用时间。

    A. The main function of epoxy putty layer is to increase the floor thickness, make it more pressure-resistant, wear-resistant and prolong the use time.


    b.固化后的环氧腻子层,表面坚硬光滑,有一定的光泽。

    B. The cured epoxy putty layer has a hard and smooth surface with a certain gloss.


    c.在环氧腻子层完全固化后,必须立即施工面层,以确保整体效果和质量。如果间隔时间过长,容易造成面漆和批土之间的不粘着和分层。

    C. After the epoxy putty layer is completely cured, the surface layer must be constructed immediately to ensure the overall effect and quality. If the interval time is too long, it is easy to cause non-adhesion and stratification between the topcoat and batch soil.


    五、面漆层施工(两道)

    5. Topcoat Construction (Two Ways)


    1、施工前保持清洁,如果杂物粘附,要清除。

    1. Keep clean before construction. If debris adheres, it should be removed.


    2、使用前应将主剂搅拌均匀。

    2. The main agent should be stirred evenly before use.


    3、按正确的比例混合主剂和固化剂,并彻底混合。

    3. Mix the main agent and curing agent in the right proportion and mix thoroughly.


    4. 用辊筒均匀涂布材料。

    4. Spread the material evenly with the roller.


    5、在30分钟内完成混合材料施工。

    5. Complete the construction of mixed materials within 30 minutes.


    6、施工交接处做好交接处理

    6. Handover treatment at construction handover


    7、施工完成后,24小时后方可上人,72小时后方可重压,以25℃为准,低温时开放时间需要根据情况适度延长。

    7. After the completion of the construction, the upper person can be placed 24 hours later, and the heavy pressure can be placed 72 hours later. The opening time at low temperature should be prolonged according to the situation.


    环氧面漆的主要作用是配色,使环氧地坪美观、光滑。同时,增加了地坪的厚度,使其更耐压和磨损,延长了使用时间。

    The main function of epoxy topcoat is color matching, which makes the floor beautiful and smooth. At the same time, it increases the thickness of the floor, makes it more resistant to pressure and wear, and prolongs the use time.


    六、滚涂耐磨清漆——罩光

    6. Rolling wear-resisting varnish-gloss


    滚涂一道耐磨清漆,提高环氧地面的光泽度,增强漆膜的硬度、可以延长环氧地坪使用寿命。

    Rolling a wear-resistant varnish can improve the gloss of epoxy floor, enhance the hardness of paint film and prolong the service life of epoxy floor.